Electrochemical cell

ABSTRACT

The electrochemical cell has an anode, a cathode, and a solid electrolyte layer. The cathode contains a perovskite oxide expressed by the general formula ABO3 and includes at least one of Sr and La at the A site as a main component. The solid electrolyte layer is disposed between the anode and the cathode. The cathode includes a solid electrolyte layer-side region within 3 μm from a surface of the solid electrolyte layer side. The solid electrolyte layer-side region includes a main phase which is configured by the perovskite oxide and a second phase which is configured by Co3O4 and (Co, Fe)3O4. An occupied surface area ratio of the second phase in a cross section of the solid electrolyte layer-side region is less than or equal to 10.5%.

CROSS-REFERENCE TO RELATED APPLICATIONS

This application is a continuation application of PCT/JP2017/027099, filed Jul. 26, 2017, which claims priority to Japanese Application No. 2016-147862, filed Jul. 27, 2016, the entire contents all of which are incorporated hereby by reference.

TECHNICAL FIELD

The present invention relates to an electrochemical cell.

BACKGROUND ART

In recent years, fuel cells that are a type of electrochemical cell have attracted attention in light of environmental problems and their effective use as an energy source.

A fuel cell generally includes an anode, a cathode, and a solid electrolyte layer disposed between the anode and the cathode.

The cathode for example is configured by a perovskite oxide such as (La, Sr)(Co, Fe)O₃: (lanthanum strontium cobalt ferrite) or the like (for example, reference is made to Japanese Patent Application Laid-Open No. 2006-32132).

SUMMARY OF INVENTION

However, fuel cell output may be reduced by repetitive power generation. The present inventors have gained the new insight that one cause of a reduction in output results from deterioration of the cathode, and that this deterioration of the cathode is related to the total proportion of Co₃O₄ and (Co, Fe)₃O₄ that is introduced into a region of the cathode on the solid electrolyte layer side.

The present invention is proposed based on the new insight above and has the object of providing an electrochemical cell that is configured to inhibit a reduction in the fuel cell output.

The electrochemical cell according to the present invention has an anode, a cathode, and a solid electrolyte layer. The cathode contains a perovskite oxide expressed by the general formula ABO₃ and includes at least one of Sr and La at the A site as a main component. The solid electrolyte layer is disposed between the anode and the cathode. The cathode includes a solid electrolyte layer-side region within 3 μm from a surface of the solid electrolyte layer side. The solid electrolyte layer-side region includes a main phase which is configured by the perovskite oxide and a second phase which is configured by Co₃O₄ and (Co, Fe)₃O₄. An occupied surface area ratio of the second phase in a cross section of the solid electrolyte layer-side region is less than or equal to 10.5%.

The present invention provides an electrochemical cell that is configured to inhibit a reduction in the fuel cell output.

BRIEF DESCRIPTION OF DRAWINGS

FIG. 1 is a cross-sectional view illustrating a configuration of a fuel cell.

DESCRIPTION OF EMBODIMENTS

Configuration of Fuel Cell 10

The configuration of the fuel cell 10 will be described making reference to the drawing. The fuel cell 10 is configured as a so-called solid oxide fuel cell (SOFC). The possible configurations of the fuel cell 10 include a flat-tubular type, a segmented-in-series type, an anode-supporting type, an electrolyte flat-plate type, a cylindrical type, or the like.

FIG. 1 is a cross-sectional view illustrating a configuration of a fuel cell 10. The fuel cell 10 includes an anode 20, a solid electrolyte layer 30, a barrier layer 40, and a cathode 50.

The anode 20 functions as an anode for the fuel cell 10. As illustrated in FIG. 1, the anode 20 includes an anode current-collecting layer 21 and an anode-active layer 22.

The anode current-collecting layer 21 is configured as a porous body that exhibits superior gas permeability. The material that constitutes the anode current-collecting layer 21 includes a material that is used in the anode current-collecting layer of a conventional SOFC, and for example, includes NiO (nickel oxide)-8YSZ (8 mol % of yttria-stabilized zirconia), or NiO—Y₂O₃ (yttria). However, when NiO is included in the anode current-collecting layer 21, at least a portion of the NiO may be reduced to Ni during the operation of the fuel cell 10. The thickness of the anode current-collecting layer 21 may be configured for example as 0.1 mm to 5.0 mm.

The anode-active layer 22 is disposed on the anode current-collecting layer 21. The anode-active layer 22 is configured as a porous body that is denser than the anode current-collecting layer 21. The material that configures the anode-active layer 22 includes use of a material used in an anode-active layer of a conventional SOFC, and for example, includes NiO-8YSZ. However, when NiO is included in the anode-active layer 22, at least a portion of the NiO may be reduced to Ni during operation of the fuel cell 10. The thickness of the anode-active layer 22 may be configured for example as 5.0 μm to 30 μm.

The solid electrolyte layer 30 is disposed between the anode 20 and the cathode 50. The solid electrolyte layer 30 in the present embodiment is sandwiched between the anode 20 and the barrier layer 40. The solid electrolyte layer 30 functions to enable the permeation of oxide ions that are produced by the cathode 50. The solid electrolyte layer 30 is configured by a material that is denser than the anode 20 or the cathode 50.

The solid electrolyte layer 30 may contain ZrO₂ (zirconia) as a main component. In addition to zirconia, the solid electrolyte layer 30 may contain an additive such as Y₂O₃ (yttria) and/or Sc₂O₃ (scandium oxide). These additives function as a stabilizing agent. The mol composition ratio (stabilizing agent:zirconia) of the stabilizing agent to zirconia in the solid electrolyte layer 30 may be configured to be approximately 3:97˜20:80. Therefore, the material used in the solid electrolyte layer 30 includes 3YSZ, 8YSZ, 10YSZ, or ScSZ (zirconia stabilized with scandia), or the like. The thickness of the solid electrolyte layer 30 for example may be configured as 3 μm to 30 μm.

In the present embodiment, the term “composition X contains as a main component composition Y” means that composition Y preferably occupies at least 70 wt % of the total of composition X, and more preferably occupies at least 90 wt %.

The barrier layer 40 is disposed between the solid electrolyte layer 30 and the cathode 50. The barrier layer 40 inhibits the formation of a high resistivity layer between the solid electrolyte layer 30 and the cathode 50. The barrier layer 40 is configured by a material that is denser than the anode 20 or the cathode 50. The barrier layer 40 may include a main component of a ceria-based material such as GDC (gadolinium-doped ceria), SDC (samarium-doped ceria), or the like. The thickness of the barrier layer 40 may be configured, for example, as 3 μm to 20 μm.

The cathode 50 is disposed on the barrier layer 40. The cathode 50 functions as a cathode for the fuel cell 10. The cathode 50 is configured as a porous body. There is no particular limitation on the porosity of the cathode 50, and it may be configured to be 20% to 60%. There is no particular limitation on the thickness of the cathode 50 and it may be configured to be 2 μm to 100 μm

The cathode 50 contains a main phase configured by a perovskite oxide expressed by the general formula ABO₃ and includes at least one of La or Sr at the A site. The perovskite oxide for example may suitably employ a composite perovskite oxide that contains lanthanum, or SSC (samarium strontium cobaltite (Sm, Sr)CoO₃) or the like that does not contain lanthanum. However, there is no limitation in this regard. The lanthanum-containing composite perovskite oxide includes LSCF (lanthanum strontium cobalt ferrite): (La, Sr) (Co, Fe)O₃), LSF: (lanthanum strontium ferrite: (La, Sr) FeO₃), LSC: (lanthanum strontium cobaltite: (La, Sr)CoO₃), and LNF (lanthanum nickel ferrite: (La(Ni, Fe)O₃), or the like. The density of the main phase that is configured by a perovskite oxide may be configured as 5.5 g/cm³ to 8.5 g/cm³.

The cathode 50 includes a first region 51 and a second region 52 as shown in FIG. 1.

The first region 51 is an example of “a solid electrolyte layer-side region” according to the present embodiment. The first region 51 is a region within 3 μm of a solid electrolyte layer-side surface 50S of the cathode 50. In the present embodiment, since the fuel cell 10 includes a barrier layer 40, the first region 51 makes contact with the barrier layer 40 on the solid electrolyte layer-side surface 50S. The solid electrolyte layer-side surface 50S is the interface between the barrier layer 40 and the cathode 50. However, when the fuel cell 10 does not include a barrier layer 40, the first region 51 will then make contact with the solid electrolyte layer 30 on the solid electrolyte layer-side surface 50S.

When component densities in a cross section of the fuel cell 10 are mapped, the solid electrolyte layer-side surface 50S can be defined with reference to a rapid change in the element densities included in the cathode.

The first region 51 contains a main phase that is configured by a perovskite oxide expressed by the general formula ABO₃ and includes at least one of Sr and La at the A site. The occupied surface area ratio of the main phase in a cross section of the first region 51 may be configured as greater than or equal to 89.5% and less than or equal to 99.5%. In the present embodiment, the term “occupied surface area ratio of the substance Z in the cross section” denotes the ratio of the sum total surface area of a substance Z phase relative to the total surface area of a solid phase in a cross section. The method of calculating the occupied surface area ratio will be described in detail below.

The first region 51 includes a second phase that is configured by (Co, Fe)₃O₄ and Co₃O₄ that have a spinel crystalline structure. (Co, Fe)₃O₄ includes Co₂FeO₄, Co_(1.5)Fe_(1.5)O₄, and CoFe₂O₄, or the like. In the second phase, Co₃O₄ and (Co, Fe)₃O₄ are in a mixed configuration and not in solid solution. More specifically, a feature such as “Co₃O₄ and (Co, Fe)₃O₄ are mixed” means a configuration in which an EDX spectrum detecting Co and O and an EDX spectrum detecting Co, Fe and O are separately acquired at different sites, and Co₃O₄ and (Co, Fe)₃O₄ are literally mixed (=present in a combined state) (Kojien Second Edition, Corrected Version, 15 Oct. 1979, Fourth Publication)). The density of the second phase may be configured as 5.2 g/cm³ to 6.2 g/cm³. The density of the second phase is less than the density of the main phase.

The occupied surface area ratio of the second phase in a cross section of the first region 51 is less than or equal to 10.5%. The occupied surface area ratio of the second phase is the sum of the occupied surface area ratio of Co₃O₄ and the occupied surface area ratio of (Co, Fe)₃O₄. More specifically, the occupied surface area ratio of the second phase includes the occupied surface area ratio of the particles that are configured by Co₃O₄, the occupied surface area ratio of the particles that are configured by (Co, Fe)₃O₄, the occupied surface area ratio of the particles that are configured by a mixture of Co₃O₄ and (Co, Fe)₃O₄ and the occupied surface area ratio of Co₃O₄ and/or (Co, Fe)₃O₄ that are mixed into the particles of the main phase.

Since the inactive part of the inner portion of the first region 51 is reduced by a configuration in which the occupied surface area ratio of the second phase is less than or equal to 10.5%, it is possible to suppress a reduction in the output of the fuel cell 10 during power supply.

It is more preferred that the occupied surface area ratio of the second phase in a cross section of the first region 51 is greater than or equal to 0.5%. In this manner, since the sintering characteristics of the first region 51 are improved by suitably introducing the second phase, the porous framework structure can be strengthened. As a result, since changes in the microstructure of the first region 51 can be inhibited, it is possible to suppress peeling of the first region 51 during power supply.

Although there is no particular limitation in relation to the ratio of the occupied surface area ratio of Co₃O₄ and the occupied surface area ratio of (Co, Fe)₃O₄ in the occupied surface area ratio of the second phase, a configuration in which (Co, Fe)₃O₄ is added in a greater amount than Co₃O₄ is effective for strengthening the framework structure of the first region 51. For that purpose, the occupied surface area ratio of (Co, Fe)₃O₄ is preferably greater than the occupied surface area ratio of Co₃O₄. The occupied surface area ratio of Co₃O₄ in a cross section of the first region 51 may be configured as less than or equal to 2.5%, and the occupied surface area ratio of (Co, Fe)₃O₄ in a cross section of the first region 51 may be configured as less than or equal to 9.5%.

Although there is no particular limitation in relation to the average equivalent circle diameter of the second phase in the cross section of the first region 51, it is preferably greater than or equal to 0.05 μm and less than or equal to 0.5 μm. In this manner, it is possible to suppress a reduction in the output of the fuel cell 10 during power supply. The average equivalent circle diameter is the value of the arithmetic average of 50 randomly selected circle diameters that have the same surface area as the second phase. The 50 second phases that are the object of the equivalent circle diameter measurement are preferably selected in a random manner from 5 or more positions on an FE-SEM image (magnification 10000 times) on a cross section of the cathode 50.

The first region 51 may include a third phase distinct from the main phase and second phase described above. The components that constitute the third phase may include CoO (cobalt oxide), SrO (strontium oxide), SrSO₄ (strontium sulfate), and an oxide of an element that constitutes the main phase. However, there is no limitation in this regard. The sum total occupied surface area ratio of the third phase in the cross section of the cathode 50 is preferably less than 10%.

The second region 52 contains a main phase that is configured by a perovskite oxide expressed by the general formula ABO₃ and includes at least one of Sr and La at the A site. Although there is no particular limitation in relation to the occupied surface area ratio of the main phase in a cross section of the second region 52, it may be configured as greater than or equal to 89.5% and less than or equal to 100%.

The second region 52 may not include a second phase that is configured by (Co, Fe)₃O₄ and Co₃O₄, or may include a second phase. Experimental confirmation has been carried out in relation to the feature that it is effective to limit the occupied surface area ratio of the second phase in a cross section of the first region 51 as described above to a predetermined range irrespective of the presence or absence of a second phase in a cross section of the second region 52 or the dimension of an occupied surface area ratio of a second phase in a cross section of the second region 52.

Method of Calculation of Occupied Surface Area of Second Phase

Now, the method of calculation of the occupied surface area ratio of the second phase in a cross section of the first region 51 will be described.

Firstly, a cross section of the cathode 50 is polished with precision machinery followed by an ion milling process performed using an IM4000 manufactured by Hitachi High-Technologies Corporation.

Then, an SEM image of a cross section of the first region 51 that is enlarged with a magnification of 10,000 times is obtained by use of a field emission scanning electron microscope (FE-SEM) that uses an in-lens secondary electron detector.

Next, 3 values corresponding to the contrast of the main phase, second phase and pores are assigned by categorizing the luminosity of the SEM image into 256 gradations. For example, the main phase is displayed as faint gray, the second phase as gray and the pores as black. However, there is no limitation in this regard.

Next, an analysis image highlighting Co₃O₄ and (Co, Fe)₃O₄ is obtained by image analysis of an SEM image using HALCON image analysis software produced by MVTec GmbH (Germany). The total surface area of Co₃O₄ and (Co, Fe)₃O₄ in the analysis image is taken to be the total surface area of the second phase, and the occupied surface area ratio of the second phase is calculated by dividing the total surface area of the second phase by the total surface area of the total solid phase in the analysis image. The analysis described above is performed at 5 positions on the same cross section of the first region 51, and a value that is the arithmetic average of the ratio of the total surface area of the second phase calculated respectively at 5 positions is the occupied surface area ratio of the second phase in the first region 51.

The respective occupied surface area ratio of Co₃O₄ and (Co, Fe)₃O₄ can be confirmed by component analysis as described below.

Firstly, the position of the second phase is confirmed with reference to the SEM image used in the calculation of the occupied surface area ratio of the second phase. Next, an EDX spectrum at the position of the second phase is obtained using energy dispersive X-ray spectroscopy (EDX). The elements that are present at the position of the second phase are identified by semi-quantitative analysis of the EDX spectrum. In this manner, it can be confirmed that Co₃O₄ and (Co, Fe)₃O₄ are in a mixed configuration in the second phase and not present in a solid solution, and that the occupied surface area ratio of Co₃O₄ and the occupied surface area ratio (Co, Fe)₃O₄ in the second phase can be separately obtained.

Whether (Co, Fe)₃O₄ is configured as any of CoFe₂O₄, Co_(1.5)Fe_(1.5)O₄ or Co₂FeO₄ can be confirmed by analysis of the crystalline structure of the second phase (lattice constant, lattice type, crystal orientation) using selected area electron diffraction (SAED) with a transmission electron microscope (TEM).

The calculation method of the occupied surface area ratio for the second phase has been described above, and the occupied surface area ratio for the main phase may be calculated in the same manner.

Cathode Material

The material used to configure the second region 52 in the cathode 50 is a perovskite oxide raw powder that is expressed by the general formula ABO₃.

The material used to configure the first region 51 in the cathode 50 is a mixture in which a Co₃O₄ raw powder and a (Co, Fe)₃O₄ raw powder are added to a perovskite oxide raw powder that is expressed by the general formula ABO₃.

The composite perovskite oxide raw powder includes a raw powder such as LSCF, LSF, LSC, LNF, SSC, or the like. (Co, Fe)₃O₄ includes a raw powder of Co₂FeO₄, Co_(1.5)Fe_(1.5)O₄ or CoFe₂O₄, or the like.

The total added amount of the Co₃O₄ raw powder and (Co, Fe)₃O₄ raw powder that is added to the material for the first region 51 is less than or equal to 9.5 wt %. In this manner, it is possible to inhibit the occupied surface area ratio of the second phase in a cross section of the first region 51 to less than or equal to 10.5%.

The total added amount of Co₃O₄ and (Co, Fe)₃O₄ in the material for the first region 51 is preferably greater than or equal to 0.46 wt %. In this manner, it is possible to control the occupied surface area ratio of the second phase in a cross section of the first region 51 to greater than or equal to 0.5%.

The occupied surface area ratio of the second phase in a cross section of the first region 51 can be minutely adjusted by adjusting the granularity of each raw powder or the configuration of the Co₃O₄ raw powder and (Co, Fe)₃O₄ raw powder (whether in an oxide or chloride configuration, or the like).

Adjusting the granularity of the Co₃O₄ raw powder and the (Co, Fe)₃O₄ raw powder enables the adjustment of the average equivalent circle diameter of the second phase in a cross section of the first region 51. Adjusting the granularity of the Co₃O₄ raw powder and the (Co, Fe)₃O₄ raw powder is preferably performed by use of an air classifier. In this manner, accurate classification such as an upper limiting value and a lower limiting value for the grain diameter is possible.

Method of Manufacturing Fuel Cell 10

Next, an example will be described of a manufacture method for the fuel cell 10. In the following description, the term “green body” denotes a member prior to firing.

Firstly, a slurry for the anode current-collecting layer is prepared by adding a binder (for example polyvinyl alcohol) to a mixture of an anode current-collecting layer powder (for example, an NiO powder and a YSZ powder) and a pore-forming agent (for example, PMMA (polymethylmethacrylate resin)). Next, an anode current-collecting layer powder is obtained by drying and granulating the slurry for the anode current-collecting layer in a spray drier. Then, a green body for the anode current-collecting layer 21 is formed by molding the anode powder using a die press molding method. At that time, a tape lamination method may be used in substitution for the die press molding method.

Next, a slurry for the anode-active layer is prepared by adding a binder (for example polyvinyl alcohol) to a mixture of an anode-active layer powder (for example, an NiO powder and a YSZ powder) and a pore-forming agent (for example, PMMA). Then, a green body for the anode-active layer 22 is formed by printing the slurry for the anode-active layer onto the green body for the anode current-collecting layer 21 using a printing method. In that manner, a green body for the anode 20 is formed. At that time, a tape lamination method or coating method or the like may be used in substitution for the printing method.

Next, a slurry for the solid electrolyte layer is prepared by mixing a mixture of water and a binder into a solid electrolyte layer powder (for example, a YSZ powder) in a ball mill. Then, a green body for the solid electrolyte layer 30 is formed by coating and drying the slurry for the solid electrolyte layer onto the green body for the anode 20. At that time, a tape lamination method or printing method or the like may be used in substitution for the coating method.

Next, a slurry for the barrier layer is prepared by mixing a mixture of water and a binder into a barrier layer powder (for example, a GDC powder) in a ball mill. Then, a green body for the barrier layer 40 is formed by coating and drying the slurry for the barrier layer onto the green body for the solid electrolyte layer 30. At that time, a tape lamination method or printing method or the like may be used in substitution for the coating method.

Next, a laminated body using the green bodies respectively for the anode 20, the solid electrolyte layer 30 and the barrier layer 40 are cofired (1300 to 1600 degrees C. for 2 to 20 hours) to form a cofired body of the anode 20, the solid electrolyte layer 30 and the barrier layer 40.

Next, a first region slurry is prepared by mixing water and a binder with the first region material described above in a ball mill. Next, a green body for the first region 51 is formed by coating and drying the first region slurry onto the barrier layer 40 of the cofired body.

Next, a second region slurry is prepared by mixing water and a binder with the second region material described above in a ball mill. Next, the second region slurry is coated and dried onto the green body for the first region 51.

Then, the green bodies for the first region 51 and the second region 52 are fired (1000 to 1100 degrees C. for 1 to 10 hours) in an electrical furnace (oxygen-containing atmosphere) to thereby form the cathode 50 on the barrier layer 40.

Other Embodiments

Although an embodiment of the present invention has been described above, the present invention is not limited to the above embodiment, and various changes or modifications may be added within a scope that does not depart from the spirit of the invention.

Although a configuration has been described in which the cathode 50 according to the present invention is applied to the fuel cell 10, in addition to a fuel cell, the cathode of the present invention may be applied to an electrochemical cell having a solid oxide configuration that includes a solid oxide-type electrolytic cell.

In the present embodiment, although the fuel cell 10 comprises the anode 20, the solid electrolyte layer 30, the barrier layer 40 and the cathode 50, there is no limitation in this regard. The fuel cell 10 may comprise the anode 20, the solid electrolyte layer 30, and the cathode 50, or another layer may be interposed between the anode 20 and the solid electrolyte layer 30, or between the solid electrolyte layer 30 and the cathode 50.

Examples

Although the examples of a cell according to the present invention will be described below, the present invention is not thereby limited to the following examples.

Preparation of Samples No. 1 to No. 21

A fuel cell according to Samples No. 1 to No. 21 was prepared as described below.

Firstly, an anode current-collecting layer (NiO:8YSZ=50:50 (Ni volume % conversion)) was formed with a thickness of 500 μm using a die press molding method, and on that layer, an anode-active layer (NiO:8YSZ=45:55 (Ni volume % conversion)) was formed using a printing method with a thickness of 20 μm.

Then a green body for a GDC layer and an 8YSZ layer were sequentially formed using a coating method on the anode-active layer and co-fired (1400 degrees C., 2 hours).

Next, as shown in Table 1, a material to configure the first region on the solid electrolyte layer side of the cathode was prepared as a first region material that includes a main phase (LSCF, LSF or SSC) and a second phase (Co₃O₄ and (Co, Fe)₃O₄). As shown in Table 1, the occupied surface area ratio of the second phase in the first region was varied by varying the addition amount of the second phase in each sample. Furthermore, the granularity of the Co₃O₄ raw powder and the (Co, Fe)₃O₄ raw powder was adjusted so that the average equivalent circle diameter of the second phase took the values shown in Table 1. In Sample No. 1, No. 2, No. 11, and No. 12, Co₂FeO₄ was used as (Co, Fe)₃O₄, in Sample No. 3 to No. 5, No. 13, No. 14, and No. 17, Co_(1.5)Fe_(1.5)O₄ was used as (Co, Fe)₃O₄, and in Sample No. 6 to No. 10, No. 15, No. 16 and No. 18 to No. 21, CoFe₂O₄ was used as (Co, Fe)₃O₄.

Next, a first region slurry was prepared by mixing the first region material, water and PVA in a ball mill for 24 hours.

Next, a green body for the first region was formed by coating and drying the first region slurry onto the GDC layer of the cofired body. At that time, the thickness after firing was configured to 3 μm by adjusting the coating amount of the first region slurry.

Next, a second region slurry was prepared by mixing the LSCF, water and a binder in a ball mill for 24 hours.

Next, a green body for the second region was formed by coating and drying the second region slurry onto the green body for the first region.

A cathode was formed by firing the green bodies for the first region and the second region for one hour in an electrical furnace (oxygen-containing atmosphere, 1000 degrees C.).

Measurement of Occupied Surface Area Ratio of Second Phase

Firstly, after polishing a cross section of the cathode in each sample with precision machinery, ion milling processing was performed using an IM4000 manufactured by Hitachi High-Technologies Corporation.

An SEM image of five positions in a cross section of the first region enlarged with a magnification of 10,000 times was obtained by use of an FE-SEM that uses an in-lens secondary electron detector. The SEM image was obtained using an FE-SEM (model: ULTRA55 manufactured by Zeiss AG) with a working distance setting of 3 mm and an acceleration voltage of 1 kV. In the SEM image, 3 values were assigned in relation to the contrast of the main phase, the second phase and the pores by categorizing the luminosity of the image into 256 gradations.

Then, the SEM image was configured as an analysis image by use of HALCON image analysis software produced by MVTec GmbH (Germany) in order to obtain an analysis image that highlights Co₃O₄ and (Co, Fe)₃O₄.

Then, the occupied surface area ratio of the second phase was calculated respectively at five positions by dividing the total surface area of Co₃O₄ and (Co, Fe)₃O₄ in the analysis image by the total surface area of the solid phase in the analysis image and then calculating the arithmetic average of those values as the occupied surface area ratio for the second phase. Furthermore, an occupied surface area ratio of Co₃O₄ and an occupied surface area ratio of (Co, Fe)₃O₄ in the second phase were separately obtained by acquiring an EDX spectrum at the position of the second phase with reference to the SEM image. The calculation results for the occupied surface area ratio of the second phase in a cross section of the first region are shown in Table 1.

Average Equivalent Circle Diameter of Second Phase

The average equivalent circle diameter of the second phase at 50 arbitrarily selected positions was calculated with reference to the 5 analysis images used in the calculation of the occupied surface area ratio. The calculation results for the average equivalent circle diameter of the second phase are shown in Table 1.

Measurement of Fuel Cell Output

While supplying nitrogen gas to the anode side and air to the cathode side of each sample, the temperature was increased to 750 degrees C. When reaching a temperature of 750 degrees C., hydrogen gas was supplied for 3 hours the anode to perform reduction process.

Next, a rated current density value of 0.2 A/cm² was set, and power generation for 1000 hours was performed while measuring the cell voltage. The voltage drop ratio per 1000 hours was calculated as a deterioration rate.

After 1000 hours of power generation, a cross section of the first region of the cathode was observed using an electron microscope to observe peeling at the interface of the first region and the barrier layer. Those samples that were observed to have peeling of less than or equal to 5 μm that has a slight effect on the characteristics of the fuel cell are designated in Table 1 as being “present (slightly).”

TABLE 1 Occupied Surface Occupied Surface Occupied Surface Average Equivalent Area Ratio Area Ratio Area Ratio Circle Diameter of Second Phase of Co₃0₄ of (Co,Fe)₃0₄ of Second Phase in Cross Section in Cross Section in Cross Section in Cross Section Main Phase of Second Phase of of First Region of First Region of First Region of First Region Sample First Region First Region (%) (%) (%) (μm) No. 1 LSCF Co₂FeO₄ + Co₃O₄ 0.2 0.05 0.15 0.35 No. 2 LSCF Co₂FeO₄ + Co₃O₄ 0.6 0.08 0.52 0.25 No. 3 LSCF Co_(1.5)Fe_(1.5)O₄ + Co₃O₄ 0.5 0.1 0.4 0.05 No. 4 LSCF Co_(1.5)Fe_(1.5)O₄ + Co₃O₄ 1.5 0.3 1.2 0.22 No. 5 LSCF Co_(1.5)Fe_(1.5)O₄ + Co₃O₄ 2.4 0.3 2.1 0.26 No. 6 LSCF CoFe₂O₄ + Co₃O₄ 5.3 0.6 4.7 0.28 No. 7 LSCF CoFe₂O₄ + Co₃O₄ 7.5 1.6 5.9 0.42 No. 8 LSCF CoFe₂O₄ + Co₃O₄ 9.7 1.8 7.9 0.50 No. 9 LSCF CoFe₂O₄ + Co₃O₄ 10.5 1.7 8.8 0.52 No. 10 LSCF CoFe₂O₄ + Co₃O₄ 11.3 1.8 9.5 0.93 No. 11 LSF Co₂FeO₄ + Co₃O₄ 0.25 0.05 0.2 0.37 No. 12 LSF Co₂FeO₄ + Co₃O₄ 1.6 0.3 1.3 0.42 No. 13 LSF Co_(1.5)Fe_(1.5)O₄ + Co₃O₄ 3.5 0.6 2.9 0.48 No. 14 LSF Co_(1.5)Fe_(1.5)O₄ + Co₃O₄ 9.5 1.6 7.9 0.50 No. 15 LSF CoFe₂O₄ + Co₃O₄ 10.2 1.5 8.7 0.55 No. 16 LSF CoFe₂O₄ + Co₃O₄ 11.5 0.6 10.9 0.97 No. 17 SSC Co_(1.5)Fe_(1.5)O₄ + Co₃O₄ 0.4 0.1 0.3 0.17 No. 18 SSC CoFe₂O₄ + Co₃O₄ 0.6 0.1 0.5 0.08 No. 19 SSC CoFe₂O₄ + Co₃O₄ 2.9 0.5 2.4 0.30 No. 20 SSC CoFe₂O₄ + Co₃O₄ 5.6 0.5 5.1 0.40 No. 21 SSC CoFe₂O₄ + Co₃O₄ 10.9 0.6 10.3 0.58 Occupied Surface Area Ratio of Second Phase in Cross Section Deterioration Presence/Absence Second Phase of of Second Region Rate of Sample Second Region (%) (%) Interface Peeling Evaluation No. 1 None 0.00 0.62 Present (Slightly) ◯ No. 2 None 0.00 0.35 No ⊚ No. 3 None 0.00 0.4 No ⊚ No. 4 None 0.00 0.47 No ⊚ No. 5 None 0.00 0.58 No ⊚ No. 6 None 0.00 0.76 No ⊚ No. 7 None 0.00 0.95 No ⊚ No. 8 None 0.00 1.1 No ⊚ No. 9 None 0.00 1.5 No ⊚ No. 10 None 0.00 2.6 Yes X No. 11 None 0.00 0.39 Present (Slightly) ◯ No. 12 None 0.00 0.85 No ⊚ No. 13 None 0.00 1.4 No ⊚ No. 14 None 0.00 1.05 No ⊚ No. 15 None 0.00 1.5 No ⊚ No. 16 None 0.00 2.8 Yes X No. 17 None 0.00 0.45 Present (Slightly) ◯ No. 18 None 0.00 0.68 No ⊚ No. 19 None 0.00 0.31 No ⊚ No. 20 None 0.00 0.78 No ⊚ No. 21 None 0.00 2.3 Yes X

As shown in Table 1, a reduction in the output of the fuel cell was suppressed in Sample No. 1 to No. 9, No. 11 to No. 15, and No. 17 to No. 20 in which the occupied surface area ratio of the second phase in a cross section of the first region of the cathode was suppressed to less than or equal to 10.5%. This feature is due to the reduction in the inactive part in an inner portion of the first region.

In the present embodiment, the effect of the present invention was simply confirmed by preparing a cathode into which a second phase had been introduced into a first region and measuring a deterioration rate after 1000 hours power generation immediately after manufacture of the fuel cell. However, the results of the present embodiment demonstrate that it is possible to suppress an output reduction of a fuel cell if the occupied surface area ratio of a second phase in a cross section of the first region is suppressed to less than or equal to 10.5% irrespective of the manner of manufacturing or the degree to which the fuel cell is used.

Furthermore, the peeling of the first region was suppressed in Sample No. 2 to No. 9, No. 12 to No. 15, and No. 18 to No. 20 in which the occupied surface area ratio of the second phase in a cross section of the first region was configured to be greater than or equal to 0.5%. This feature is due to the strengthening of the porous framework structure by improving the sintering characteristics of the first region with the second phase.

The occupied surface area ratio of (Co, Fe)₃O₄ in those samples is generally greater than the occupied surface area ratio of Co₃O₄, and therefore such a feature exhibits a more useful effect in relation to the strengthening of the framework structure of the cathode. However, even when the occupied surface area ratio of (Co, Fe)₃O₄ is smaller than the occupied surface area ratio of Co₃O₄, or even when it is the same, the framework structure of the cathode can be strengthened by a configuration in which the occupied surface area ratio of the second phase is greater than or equal to 0.5%.

In the present embodiment, the effect of the present invention was simply confirmed by preparing a cathode into which a second phase is introduced and observing the peeling of the first region after 1000 hours power generation immediately after manufacture of the fuel cell. However, the results of the present embodiment demonstrate that it is possible to suppress the production of cracks in a cathode if the occupied surface area ratio of the second phase in a cross section of the first region is configured to be greater than or equal to 0.5%, irrespective of the manner of manufacturing or the degree of to which the fuel cell is used.

In addition, a further suppression in a reduction of fuel cell output was enabled in Sample No. 1 to No. 8, No. 11 to No. 14, and No. 17 to No. 20 in which the average equivalent circle diameter of the second phase in a cross section of the first region was configured to be greater than or equal to 0.05 μm and less than or equal to 0.5 μm.

In the present embodiment, although those samples in which the second region does not contain the second phase were evaluated, even when the second region contains the second phase, the above results have been experimentally confirmed to be available irrespective of the dimension of the occupied surface area ratio of the second phase in a cross section of the second region. 

The invention claimed is:
 1. An electrochemical cell comprising: an anode, a cathode containing a perovskite oxide expressed by the general formula ABO₃ and including at least one of Sr and La at the A site as a main component, and a solid electrolyte layer disposed between the anode and the cathode, the cathode including a solid electrolyte layer-side region within 3 μm from a surface of the solid electrolyte layer side, the solid electrolyte layer-side region including a main phase which is configured by the perovskite oxide and a second phase which is configured by Co₃O₄ and (Co, Fe)₃O₄, an occupied surface area ratio of the second phase in a cross section of the solid electrolyte layer-side region being less than or equal to 10.5%, and an occupied surface area ratio of (Co, Fe)₃O₄ in a cross section of the solid electrolyte layer-side region is greater than an occupied surface area ratio of Co₃O₄.
 2. The electrochemical cell according to claim 1, wherein the occupied surface area ratio of the second phase in a cross section of the solid electrolyte layer-side region is greater than or equal to 0.5%.
 3. The electrochemical cell according to claim 1, wherein an average equivalent circle diameter of the second phase in a cross section of the solid electrolyte layer-side region is greater than or equal to 0.05 μm and less than or equal to 0.5 μm.
 4. The electrochemical cell according to claim 1, wherein the occupied surface area ratio of the second phase in a cross-section of the solid electrolyte layer-side region is from 0.5-9.7%.
 5. The electrochemical cell according to claim 4, wherein the occupied surface area ratio of the second phase in a cross-section of the solid electrolyte layer-side region is from 0.6-2.9%. 